Middle margin PET film with double sided Al metallized
You are here: Home » Products » Middle margin PET film with double sided Al metallized
Share to:

Middle margin PET film with double sided Al metallized

Quantity:
  • mpp film
  • saifu

H)1)UG$S$B@QT[HRH3P{)CN 

基膜Base film

聚酯PET

常规厚度Normal thickness

5.0μm ~12.0μm

留边形式Margin type

中留边Middle

蒸镀金属Coating metal

Aluminum

蒸镀面Coating side

双面 Double

边缘结构Edge structure

无边缘加厚 No heavy edge

 

方块电阻 Square resistance                     

方阻

Square resistance

偏差范围

Tolerance

1.5Ω/

±30%

2.0Ω/

±30%

2.5Ω/

±30%



常用产品规格(宽度和留边量)

 Normal film Width and Margin


X`(%U_[S``I}4Z7]HW$BCPC




  

备注:可根据客户需求定制所需方阻、宽度与留边。

Note: If customer needs other resistance, film width or margin, please contact us.

 

膜卷内外径 Inside/outside core diameter

膜卷内径及允许偏差

Inside core diameter/Tolerance

膜卷外径及允许偏差

Outside core diameter/Tolerance

75mm

+1/-0.5mm

175

220

±25mm

±20mm

备注:同一对膜外径偏差≤2mm

Note: A pair tolerance of outside core diameter 2mm.

金属化膜技术参数Specifications of metallized film

金属化聚丙烯薄膜(MPP Film)

性能

Properties

单位

Unit

典型值

Typical value

密度Density

g/cm3

0.905±0.005

厚度 Thickness

µm

2.2  15

抗拉强度Tensile Strength

纵向MD (MPa)

100

断裂伸长率Elongation at Break

纵向MD (%)

20200

弹性模量Elastic Modulus

纵向MD (MPa)

2800

热收缩率Heat Shrinkage

纵向MD (%)

5 ( 120°C, 10min)

湿润张力Wetting Tension

mN/m

38  (电晕处理面Corona treated side)

表面粗糙度Surface Roughness

µm

0.08

熔点Melting Point

172

体积电阻率Volume Resistivity

Ω.m

1015

介电强度Break-dowm Voltage

V/µm

350 ( 23°C, DC )

相对介电常数Dielectric Constant


2.2  (20℃,1KHz)

介电损耗因数Dissipation Factor


4×10-4 (20℃,1KHz )

RC

ΩF

5×104

 

金属化聚酯薄膜(MPET Film)

性能

Properties

单位

Unit

典型值

Typical value

密度Density

g/cm3

1.4

厚度 Thickness

µm

5

512

12

抗拉强度Tensile Strength

纵向MD (MPa)

84

108

120

断裂伸长率Elongation at Break

纵向MD (%)

22

33

44

弹性模量Elastic Modulus

纵向MD (MPa)

3500

介电强度Break-dowm Voltage

V/µm

200 

( 23°C, DC )

250 

( 23°C, DC )

热收缩率Heat Shrinkage

纵向MD (%)

2.5 ( 150°C, 10min)

表面粗糙度Surface Roughness

µm

0.095

熔点Melting Point

256

体积电阻率Volume Resistivity

Ω.m

1015 

 ( 23°C, 相对湿度Humidity 50%)

相对介电常数Dielectric Constant


3.2

 (20℃,1KHz)

介电损耗因数Dissipation Factor

-

60×10-4 

(20℃,1KHz )

RC

ΩF

1×104

Ø Film rolls are packed and heat-sealed in vacuum plastic bags with desiccants inside.

Ø The Bags are marked with type labels, mark thickness width, free margin width and resistance.

Ø The bags are packed in carton cases.

The cartons are wrapped by wooden cases or reinforced carton.

BK0X(C`01I(2XQ7SJV36%EB5QY`@MZZYZ}{PCR7X)FXNP(AUF%B}H7ZO8%{JO[2GNNS5QY`@MZZYZ}{PCR7X)FXN)KUQXIE3BZ1JWRC1O_NV$4E

Ø Metallized film should be stored in its original package with temperature - 35 and humidity less than 85%RH before using.

Ø Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.

Ø The recommended temperature is 15 -25 with humidity less than 60%RH after opening

Ø With original sealed package, and stored as mentioned above, the storage time can be as following:

Al metallized film: 12 months from the delivery date. Al/Zn Alloy metallized film: As zinc is quite unstable , the storage period (from delivery date) depends on the resistance of the film:

10 Ω/6 months

10 ~30Ω/3 months

>30Ω/: 1month 



Related Products

content is empty!

QUICK LINKS

PRODUCTS

CONTACT US

Add: No.1771 Qifeng Road,Shizishan National High Technology Zone,Tongling City, Anhui Province,China
Mob: +86-13305628091
Tel: +86-562-2828238
Email: vivien@anhuisafe.com

SOCAIL NETWORK

NEWSLETTER

Copyright © 2018. Anhui Safe Electronics Co.,Ltd. All rights reserved.    Sitemap   Support by Leadong 
keywords:inkjet pvc card|inkjet pvc card|inkjet pvc card|inkjet pvc card|inkjet pvc card|inkjet pvc card a frame signs